POM+MoS2 Sheet/Rod
Color：White, Black
Size: POM+Mos2 Sheet：T X WX L 0.5-100mm×620/1000mm×1230/2000mm
POM+Mos2 ROD：Dia. X L 6-100mm×1000/2000mm
DATA SHEET
|
ITEM |
METHOD |
UNIT |
VALUE |
|
Autai POM+Mos2 Mechanical Properties |
|||
|
Specific gravity |
ASTM D792 |
g/cm3 |
1.46 |
|
Tensile yield strength |
ASTM D638 |
Mpa |
64 |
|
Breaking elongation |
ASTM D638 |
% |
20 |
|
Bending strength |
ASTM 790 |
Mpa |
84 |
|
Flexural modulus |
ASTM 790 |
Mpa |
2800 |
|
Shore hardness |
ASTM D2240 |
D |
85 |
|
Impact strength |
ASTM D256 |
J/M |
50 |
|
Autai POM+Mos2 Thermal Properties |
|||
|
Melting point |
DSC |
℃ |
190 |
|
Heat distortion temperature |
ASTM D648 |
℃ |
130 |
|
Operating temperature |
- |
℃ |
100 |
|
Maximum operating temperature |
- |
℃ |
150 |
|
Thermal conductivity |
DIN 52612-1 |
W/(K-M) |
0.33 |
|
Coefficient of linear thermal expansion |
ASTM D696 |
10-5-1/K |
1.3 |
|
Autai POM+Mos2 Electrical Properties |
|||
|
Dielectric strength |
ASTM D150 |
KV-mm |
- |
|
Dielectric loss factor |
ASTM D150 |
- |
- |
|
Volume resistivity |
ASTM D257 |
Ω.cm |
1014 |
|
Surface resistivity |
ASTM D257 |
Ω |
1016 |
|
Dielectric constant |
ASTM D149 |
- |
- |
|
Autai POM+Mos2 Chemical Properties |
|||
|
Water absorption |
23℃ 60%RH |
% |
0.5 |
|
Acid resistance |
23℃ 60%RH |
|
+ |
|
Alkali resistance |
|
|
+ |
|
Acid and alkali resistance |
|
|
+ |
|
Resistance to sodium chlorate |
|
|
0 |
|
Resistance toaromatic compounds |
|
|
+ |
|
Resistance to ketone |
23℃ 60%RH |
|
+ |
|
Resistance to hot water |
23℃ 60%RH |
|
+ |
|
Others |
|||
|
Flammability |
UL 94 |
|
HB |
|
Viscosity |
- |
|
+ |
|
Non toxic |
EEC 90/128 FDA |
|
+ |
|
Coefficient of friction |
DIN 53375 |
|
+ |
|
Anti-ultraviolet |
- |
|
0 |
Remarks:
1.“+”: positive “-”: negative “0”: depends.
2. All POM+Mos2 the parameters above are based on raw material but not finished products,